High-temperature thermoelectric properties of Ca1 xPrxMnO3 d ð0pxo1Þ / Phung, ThanhPQ

Tác giả : Phung, ThanhPQ

Nhà xuất bản : Elsevier

Năm xuất bản : 2004

Chủ đề : 1. Thermoelectric properties. 2. Article.

Chia sẻ

Thông tin chi tiết

Tóm tắt :

Ca1 xPrxMnO3 d (x=0, 0.05, 0.15, 0.1, 0.2, 0.4, 0.67;d=0.02) samples were prepared by a solid-state reaction method. X-ray diffraction analysis showed that all samples prepared were of single phase with orthorhombic structure. Electrical resistivity measurements from room temperature to 1300 K showed that a metallic conducting tendency dominated at high temperatures. The hopping nature of the charge carriers was well interpreted in the framework of polaron theory. The Seebeck coefficient was measured in the same temperature interval, and its concentration dependence was analyzed using the high-temperature (HT) thermopower theory proposed by Marsh–Parris. The thermal conductivity and the figure of merit of the prepared samples were also compared with those of other similar perovskite compounds. The observed figure of merit of the sample withx=0.15 wasZ=1.5 10 4 K 1 atT=1100 K, indicating a good potential for application as a HT thermoelectric material.
Chia sẻ


Hiển thị MARC

 Thông tin dữ liệu nguồn

 Thư viện  Ký hiệu xếp giá  Dữ liệu nguồn
Viện Tài nguyên và Môi trường - ĐHQGHN
https://repository.vnu.edu.vn/handle/VNU_123/10149